Silane-containing carboxy-terminated polymers

ABSTRACT

The present invention relates to and group-functionalized polymers having, at the and of the polymer chain, a sliane-containing carboxyl group of the formula (I) 
     
       
         
         
             
             
         
       
     
     where
         R 1 , R 2  are the same or different and are each an H, alkyl, alkoxy, cycloalkyl, cycloalkoxy, aryl, aryloxy, alkaryl, alkaryloxy, aralkyl or aralkoxy radical which may contain one or more heteroatoms, preferably O, N, S or Si,   R 3 , R 4  are the same or different and are each an H, alkyl, cycloalkyl, aryl, alkaryl or aralkyl radical which may contain one or more heteroatoms, preferably O, N, S or Si,   A is a divalent organic radical which, as well as C and H, may contain one or more heteroatoms, preferably O, N, S or Si.

The invention relates to end group-functionalized polymers, and to the preparation and use thereof.

Important properties desirable in tyre treads include good adhesion on dry and wet surfaces, low rolling resistance and high abrasion resistance. It is very difficult to improve the skid resistance of a tyre without simultaneously worsening the rolling resistance and abrasion resistance. A low rolling resistance is important for low fuel consumption, and high abrasion resistance is a crucial factor for a long service life of the tyre.

Wet skid resistance and rolling resistance of a tyre tread depend largely on the dynamic/mechanical properties of the rubbers which are used in the blend production. To lower the rolling resistance, rubbers with a high resilience at higher temperatures (60° C. to 100° C.) are used for the tyre tread. On the other hand, for improving the wet skid resistance, rubbers having a high damping factor at low temperatures (0 to 23° C.) or low resilience in the range of 0° C. to 23° C. are advantageous. In order to fulfil this complex profile of requirements, mixtures of various rubbers are used in the tread. Usually, mixtures of one or more rubbers having a relatively high glass transition temperature, such as styrene-butadiene rubber, and one or more rubbers having a relatively low glass transition temperature, such as polybutadiene having a high 1,4-cis content or a styrene butadiene rubber having a low styrene and low vinyl content or a polybutadiene prepared in solution and having a moderate 1,4-cis and low vinyl content, are used.

Anionically polymerized solution rubbers containing double bonds, such as solution polybutadiene and solution styrene-butadiene rubbers, have advantages over corresponding emulsion rubbers in terms of production of tyre treads with low rolling resistance. The advantages lie, inter alia, in the controllability of the vinyl content and of the associated glass transition temperature and molecular branching. In practical use, these give rise to particular advantages in the relationship between wet skid resistance and rolling resistance of the tyre. Important contributions to energy dissipation and hence to rolling resistance in tyre treads result from free ends of polymer chains and from the reversible buildup and degradation of the filler network formed by the filler used in the tyre tread mixture (usually silica and/or carbon black).

The introduction of functional groups at the end of the polymer chains and/or start of the polymer chains enables physical or chemical attachment of these ends and/or starts of the polymer chains to the flier surface. This restricts the mobility thereof and hence reduces energy dissipation under dynamic stress on the tyre tread. At the same time, these functional groups improve the dispersion of the filler in the tyre tread, which can lead to a weakening of the filler network and hence to further lowering of the rolling resistance.

For this purpose, numerous methods for end group modification have been developed. For example, EP0180141A1 describes the use of 4,4′-bis(dimethylamino)benzophenone or N-methylcaprolactam as functionalizing reagents. The use of ethylene oxide and N-vinylpyrrolidone is also known from EP0884606A1. A number of further possible functionalizing reagents are detailed in U.S. Pat. No. 4,417,029. Methods for introducing functional groups at the start of polymer chains by means of functional anionic polymerization initiators are described, for example, in EP0513217A1 and EP0675140A1 (initiators with a protected hydroxyl group), US20080308204A1 (thioether-containing initiators) and in U.S. Pat. No. 5,792,820, EP0590490A1 and EP0594107A1 (alkali metal amides of secondary amines as polymerization initiators).

The carboxyl group, as a strongly polar, bidentate ligand, can interact particularly well with the surface of the silica filler in the rubber mixture. Methods for introducing carboxyl groups along the polymer chain of diene rubbers prepared in solution are known and are described, for example, in DE2653144A1, EP1000971A1 EP1050545A1, WO2009034001A1 These methods have several disadvantages, for example that long reaction times are required, that the functionalizing reagents are converted only incompletely, and that an alteration of the polymer chains occurs as a result of side reactions such as branching. Moreover, these methods do not enable particularly effective functionalization of the ends of the polymer chain.

The introduction of carboxyl groups at the chain ends of diene rubbers has likewise been described, for example in U.S. Pat. No. 3,242,129, by reaction of the anionic ends of the polymer chain with CO₂. This method has the disadvantage that the polymer solution has to be contacted with gaseous CO₂, which is found to be difficult because of the high viscosity and the resultant poor mixing. In addition, coupling reactions which are difficult to control occur as a result of reaction of more than one end of the polymer chain at the carbon atom of the CO₂. This coupling can be avoided by sequential reaction of the carbanionic ends of the polymer chain first with ethylene oxide or propylene oxide, followed by reaction of the ends of the polymer chain which are now alkoxidic with a cyclic anhydride (U.S. Pat. No. 4,465,809). Here too, however, there is the disadvantage that gaseous and additionally very toxic ethylene oxide or propylene oxide has to be introduced into the high-viscosity rubber solution. Furthermore, reaction of the alkoxidic chain ends with the cyclic anhydride forms hydrolysis-prone ester bonds which can be cleaved in the course of workup and in the course of later use.

Especially silanes and cyclosiloxanes having a total of at least two halogen and/or alkoxy and/or aryloxy substituents on silicon are of good suitability for end group functionalization of diene rubbers, since one of said substituents on the silicon atom can be readily exchanged in a rapid substitution reaction for an anionic diene and of the polymer chain and the further aforementioned substituent(s) on Si is/are available as a functional group which, optionally after hydrolysis, can interact with the filler of the tyre tread mixture. Examples of silanes of this kind can be found in U.S. Pat. No. 3,244,664, U.S. Pat. No. 4,185,042, EP0778311A1 and US20050203251A1.

These silanes generally have functional groups which are bonded directly to the silicon atom or bonded to Si via a spacer and can interact with the surface of the silica filler in the rubber mixture. These functional groups are generally alkoxy groups or halogens directly on Si, and tertiary amino substituents bonded to Si via a spacer. Disadvantages of these silanes are the possible reaction of a plurality of anionic ends of the polymer chain per silane molecule, elimination of troublesome components and coupling to form Si—O—Si bonds in the course of workup and storage. The introduction of carboxyl groups by means of these silanes has not been described,

WO2012/065908A1 describes 1-oxa-2-silacycloalkanes as functionalizing reagents for introduction of hydroxide end groups in diene polymers. These 1-oxa-2-silacycloakanes do not have the disadvantages of the silanes described in the above paragraph, such as reaction of a plurality of anionic ends of the polymer chain per silane molecule, elimination of troublesome components and coupling to form Si—O—Si bonds in the course of workup and storage. However, these functionalizing reagents also do not enable the introduction of carboxyl groups at the ends of the polymer chain.

The problem addressed was therefore that of providing carboxyl-terminated polymers which do not have the disadvantages of the prior art and more particularly enable utilization of the good reactivity of silanes having anionic ends of the polymer chain.

This problem is solved through the proposal of and group-functionalized polymers having, at the end of the polymer chain, a silane-containing carboxyl group of the formula (I)

where

-   -   R¹, R² are the same or different and are each an H, alkyl,         alkoxy, cycloalkyl, cycloalkoxy, aryl, aryloxy, alkaryl,         alkaryloxy, aralkyl or aralkoxy radical which may contain one or         more heteroatoms, preferably O, N, S or Si,     -   R³, R⁴, are the same or different and are each an H, alkyl,         cycloalkyl, aryl, alkaryl or aralkyl radical which may contain         one or more heteroatoms, preferably O, N, S or Si,     -   A is a divalent organic radical which, as well as C and H, may         contain one or more heteroatoms, preferably O, N, S or Si.

Preferably, the inventive end group-functionalized polymers may be in the form of carboxylates having end groups of the formula (a):

where

-   -   R¹, R² are the same or different and are each an H, alkyl,         alkoxy, cycloalkyl, cycloalkoxy, aryl, aryloxy, alkaryl,         alkatyloxy, aralkyl or aralkoxy radical which may contain one or         more heteroatoms, preferably O, N, S or Si,     -   R³, R⁴ are the same or different and are each an H, alkyl,         cycloalkyl, aryl, alkaryl or aralkyl radical which may contain         one or more heteroatoms, preferably O, N, S or Si,     -   A is a divalent organic radical which, as well as C and H, may         contain one or more heteroatoms, preferably O, N, S or Si, n is         an integer from 1 to 4,     -   M is a metal or semimetal of valency 1 to 4, preferably Li, Na,         K, Mg, Ca, Zn, Fe, Co, Ni, Al, Nd, Ti, Sn, Si, Zr, V, Mo or W.

Preferred polymers for preparation of the inventive end group-functionalized polymers are diene polymers, and diene copolymers obtainable by copolymerization of dienes with vinylaromatic monomers.

Preferred dienes are 1,3-butadiene, isoprene, 1,3-pentadiene, 2,3-dimethylbutadiene, 1-phenyl-1,3-butadiene and/or 1,3-hexadiene. Particular preference is given to using 1,3-butadiene and/or isoprene.

The vinylaromatic comonomers may, for example, be styrene, o-, m- and/or p-methylstyrene, p-tert-butylstyrene, α-methylstyrene, vinylnaphthalene, divinylbenizene, trivinylbenzene and/or divinylnaphthalene. Particular preference is given to using styrene.

These polymers are preferably prepared by anionic solution polymerization or by polymerization by means of coordination catalysts. In this context, coordination catalysts are understood to mean Ziegler-Natty catalysts or monometallic catalyst systems. Preferred coordination catalysts are those based on Ni, Co, Ti, Zr, Nd, V, Cr, Mo, W or Fe.

Initiators for anionic solution polymerization are those based on alkali metals or alkaline earth metals, for example methyllithium, ethyllithium, isopropyllithium, n-butyllithium, seatutyllithium, penyilithium, n-hexyllithium, cyclohexyllithium, octyllithium, decyllithium, 2-(6-lithio-n-hexoxy)tetrahydropyran, 3-(tert-butyldimethylsiloxy)-1-propyllithium, phenyllithium, 4-butylphenylithium, 1-naphthyllithium, p-tolyllithium and allyilithium compounds derived from tertiary N-allylamines, such as [1-(dimethylamino)-2-propenyljlithium, [1-[bis(phenylmethyl)amino]-2-properlyillithium, [1-(diphenylamino)-2-propenyil)lithium, [1-(1-pyrrolidinyl)-2-propenyillithium, lithium amides of secondary amines, such as lithium pyrrolidide, lithium piperidide, lithium hexamethyleneimide, lithium 1-methylimidazolidide, lithium 1-methylpiperazide, lithium morpholide, lithium dicyclohexylamide, lithium dibenzylamide, lithium diphertylamide. These allyllithium compounds and these lithium amides can also be prepared in situ by reaction of an organolithium compound with the respective tertiary N-allylamines or with the respective secondary amines. In addition, it is also possible to use di- and polyfunctional organolithium compounds, for example 1,4-dilithiobutane, dilithium piperazide. Preference is given to using n-butyllithium and seo-butyllithium.

In addition, it is possible to use the known randomizers and control agents for the microstructure of the polymer, for example diethyl ether, di-n-propyl ether, diisoprcpyl ether, di-n-butyl ether, ethylene glycol dimethyl ether, ethylene glycol diethyl ether, ethylene glycol di-n-butyl ether, ethylene glycol di-tert-butyl ether, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, diethylene glycol di-n-butyl ether, diethylene glycol di-certbutyl ether, 2-(2-elhoxyethoxy)-2-methylpropane, triethylene glycol dimethyl ether, tetrahydrofuran, ethyl tetrahydrofurfuryl ether, hexyl tetrahydrofurfuryl ether, 2,2-bis(2-tetrahydrofuryl)propane, dioxane, trimethylamine, triethyiarnine, N,N,N′,N′-tetramethylethylenediamine, N-methylmorpholine, N-ethyimorpholine, 1,2-dipiperidinoethane, 1,2-dipyrrolidinoethane, 1,2-dimorpholinoethane and potassium and sodium salts of alcohols, phenols, carboxylic acids, sulphonic acids.

Such solution polymerizations are known and are described, for example, in I, Frarita, Elastomers and Rubber Compounding Materials; Elsevier 1989, pages 113-131, in Houben-Weyl, Methoden der Organischen Chemie [Methods of Organic Chemistry], Thieme Verlag, Stuttgart, 1961, volume XIV/1 pages 645 to 673 or in volume E 20 (1987), pages 114 to 134 and pages 134 to 153, and in Comprehensive Polymer Science, Vol. 4, Part II (Pergamon Press Ltd., Oxford 1989), pages 53-108.

The preparation of the preferred diene homopolymers and diene copolymers preferably takes place in a solvent. The solvents used for the polymerization are preferably inert aprotic solvents, for example paraffinic hydrocarbons such as isomeric butanes, pentanes, hexanes, heptanes, octanes, decanes, cyclopentane, methylcyclopentane, cyclohexane, methylcyclohexane, ethylcyclohexane or 1,4-dimethylcyclohexane, or alkenes such as 1-butene, or aromatic hydrocarbons such as benzene, toluene, ethylberizene, xylene, diethylbenzene or propylbenzene. These solvents can be used individually or in combination. Preference is given to cyclohexane, methylcyclopentane and n-hexane. Blending with polar solvents is likewise possible.

The amount of solvent in the process according to the invention is typically in the range from 100 to 1000 g, preferably in the range from 200 to 700 g, based on 100 g of the total amount of monomer used. However, it is also possible to polymerize the monomers used in the absence of solvents.

The polymerization can be performed in such a way that the monomers and the solvent are initially charged and then the polymerization is started by adding the initiator or catalyst. Polymerization in a feed process is also possible, in which the polymerization reactor is filled by addition of monomers and solvent, the initiator or catalyst being initially charged or added with the monomers and the solvent, Variations such as initial charging of the solvent in the reactor, addition of the initiator or catalyst and then addition of the monomers, are possible. In addition, the polymerization can be operated in a continuous mode, Further addition of monomer and solvent during or at the end of the polymerization is possible in all cases.

The polymerization time may vary within wide limits from a few minutes to a few hours. Typically, the polymerization is performed within a period of 10 minutes up to 8 hours, preferably 20 minutes to 4 hours. It can be performed either at standard pressure or at elevated pressure (from 1 to 10 bar),

It has been found that, surprisingly, the use of one or more silalactones as functionalizing reagents can produce carboxyl-terminated polymers which do not have the disadvantages of the prior art.

The silalactones are compounds of the formula (III)

where

-   -   R¹, R² are the same or different and are each an H, alkyl,         aikoxy, cycloalkyl, cycloalkoxy, aryl, aryloxy, alkaryl,         alkaryloxy, aralkyi or aralkoxy radioed which may contain one or         more heteroatoms, preferably O, N, S or Si,     -   R³, R⁴ are the same or different and are each an H, aikyl,         cycloalkyl, aryl, alkaryl or aralkyl radical which may contain         one or more heteroatoms, preferably O, N, S or Si,     -   A is a divalent organic radical which, as well as C and H, may         contain one or more heteroatoms, preferably O, N, S or Si,         where preferably     -   R¹, R² are the same or different and are each an H,         (C₁-C₂₄)-alkoxy, (C₃-C₂₄)-cycloalkyl, (C₃-C₂₄)-cycloalkoxy,         (C₆-C₂₄)-aryl, (C₆ ⁻C₂₄)-arloxy, (C_(6-C) ₂₄)-alkaryl,         (C₆-C₂₄)-alkaryloxy, (C₅-C₂₄)-aralkyl or (C₆-C₂₄)-aralkoxy         radical which may contain one or more heteroatoms, preferably O,         N, S or Si, and     -   R³, R⁴ are the same or different and are each an H,         (C₁-C₂₄)-alkyl, (C₃-C₂₄)-cycloalkyl, (C₆-C₂₄)-aryl,         (C₆-C₂₄)-alkaryl or (C₆-C₂₄)-aralkyl radical which may contain         one or more heteroatoms, preferably O, N, S or Si.

Examples of compounds of the formula (III) are:

2,2-dimethyl-1-oxa-2-silacyclohexan-6-one (1), 2,2,4-trimethyl-l-oxa-2-silacyclohexan-6-one (2), 2,2,5-trimethyl-1-oxa-2-silacyclohexan-6-one (3), 2,2,4,5-tetramethyl-1-oxa-2-silacyclohexan-6-one (4), 2,2-diethyl-1-oxa-2-silacyclohexan-8-one (5), 2,2-diethoxy-1-oxa-2-silacyclohexan-6-one (6), 2,2-dimethyl-1,4-dioxa-2-silacyclohexan-6-one (7), 2,2,5-trimethyl-1,4-dioxa-2-silacyclohexan-6-one (8), 2,2,3,3-tetramethyl-1,4-dioxa-2-silacyclohexan-6-one (9), 2,2-dimethyl-1-oxa-4-thia-2-silacyclohexan-6-one (10), 2,2-diethyl-1-oxa-4-thia-2-silacyclohexan-6-one (11), 2,2-diphenyl-1-oxa-4-thia-2-silacyclonexan-6-one (12), 2-methyl-2-ethenyl-1-oxa-4-thia-2-silacyclohexan-6-one (13), 2,2,5-trimethyl-1-oxa-4-thia-2-silacyclohexan-6-one (14), 2,2-dimethyl-1-oxa-4-aza-2-silacyclohexan-6-one (15), 2,2,4-trimethyl-1-oxa-4-aza-2-silacyclohexan-6-one (16), 2,4-dimethyl-2-phenyl-1-oxa-4-aza-2-silacyclohexan-6-one (17), 2,2-dimethyl-4-trimethylsilyl-1-oxa-4-aza-2-silacyclohexan-8-one (18), 2,2-diethoxy-4-methyl-1-oxa-4-aza-2-silacyclohexan-6-one (19), 2,2,4,4-tetramethyl-1-oxa-2,4-disilacyclohexan-8-one (20), 3,4-dihydro-3,3-dimethyl-1H-2,3-benzoxasilin-1-one (21), 2,2-dimethyl-1-oxa-2-silacyclopentan-5-one (22), 2,2,3-trimethyl-1-oxa-2-silacyclopenten-5-one (23), 2,2-dimethyl-4-phenyl-1-oxa-2-silacyclopentan-5-one (24), 2,24(tert-butyl)-1-oxa-2-silacyclopentan-5-one (25), 2-methyl-2-(2-propen-1-yl)-1-oxa-2-silacyclopentan-5-one (26), 1,1-dimethyl-2,1-benzoxasilol-3(1H)-one (27), 2,2-dimethyl-1-oxa-2-silacycloheptan-7-one (28).

The syntheses of such silalactones are described, for example, in U.S. Pat. No. 2,635,109; M. Wieber, M. Schmidt, Chemische Berichte 1963, 96 (10), 2822-5; J. M. Wolcott, F. K. Cartledge, Journal of Organic Chemistry 1974, 39 (16), 2420-4; M. P. Sibi, J. W. Christensen, Tetrahedron Letters 1995, 36 (35), 6213-6; T. Linker, M. Maurer, F. Rebien, Tetrahedron Letters 1996, 37 (46), 8363-6; Shindo at al., Angewandte Chemie, International Edition 2004, 43 (1), 104-6.

It has been found that the inventive end group-funotionalized polymers can be prepared by reaction of reactive ends of polymer chains with silalactones and optional subsequent protonation of the oarboxylate end group produced to give the carboxyl end group.

Thus, the invention also provides for the use of silalactones as functionalizing reagents for preparation of the inventive end group-functionalized polymers having end groups of the formula (I) or (II).

When polymers having very reactive nucleophilic ends of the polymer chains are reacted with compounds of the formula (ill), the polymer chains cannot only be attached on the silicon atom of the functionalizing reagent; in addition, attachment may additionally occur on the carbonyl carbon atom. This leads to linear coupling of the polymer chains (Scheme 1). In this case, a polymer mixture is present. Polymers having very reactive ends of the polymer chains are, for example, diene homopolymers and diene copolymers, which are prepared by means of anionic polymerization or with coordination catalysts.

Coupling reactions of this kind may be desirable in some cases, in order to increase the polydispersity and in this way to influence rheological properties of the polymers, such as Mooney viscosity and cold flow, In other cases, it may be advantageous to suppress the coupling reaction, in order to obtain a maximum number of functionalized ends of polymer chains, which should have a positive effect on the dynamic-mechanical properties of the vulcanizates containing these polymers.

It has now been found that, surprisingly, the coupling reaction according to Scheme 1 can be /prevented virtually completely (<5% by weight based on the total amount of polymer) when polymers having very reactive nucleophilic ends of the polymer chains are reacted in a first step with a reagent which leads to polymers having silanol or silanolate end groups and, in a second step, these polymers having silanol or silanolate end groups are allowed to react with compounds of the formula (III) (Scheme 2). It is likewise possible to set a desired level of coupling in a controlled manner by, in a first step, reacting not all of the very reactive nucleophilic ends of the polymer chains with a reagent which leads to polymers having silanol or silanolate and groups.

Reagents of this kind which are used in the first step can lead directly or indirectly (for example via a subsequent hydrolysis of Si—Cl groups) to silanol or silanolate end groups. Preference is given, however, to reagents which give silanolate and groups in a direct reaction. Very particular preference is given to cyclosiloxanes of the formula (IV)

where R⁵, R⁶ in Scheme 2 and in formula (IV) are the same or different and are each an H, cycloaikyl, aryl, alkaryl or aralkyl radical which may contain one or more heteroatoms, preferably O, N, S or Si.

Preference is given to hexamethylcyclotrisiloxane, octamethylcyclotetrasiloxane, decamethylcyclopentasiloxane and dodecamethyicyclohexasiloxane, and to mixtures of cyclosiloxanes of different ring size.

The intermediates obtainable in Scheme 2 can be isolated by the methods known to those skilled in the art.

The inventive end group-functionalized polymers preferably have mean molar masses (number-average, M_(n)) of 10 000 to 2 000 000 g/mol, preferably of 100 000 to 1 000 000 g/mol, and glass transition temperatures of −110° C. to +20° C., preferably of −110° C. to 0° C., and Mooney viscosities [ML 1+4 (100° C.)] of 10 to 200, preferably of 30 to 150, Mooney units.

The invention further provides a process for preparing the inventive end group-functionalized polymers, in which one or more compounds of the formula (Ill) are added, as a pure substance, solution or suspension, to give polymers having reactive ends of the polymer chains. The addition preferably follows conclusion of the polymerization, but may also precede complete monomer conversion. The reaction of compounds of the formula (III) with polymers having reactive ends of the polymer chains is effected at the temperatures customarily used for the polymerization. The reaction times for the reaction of compounds of the formula (III) with the reactive ends of the polymer chains may be between a few minutes and several hours.

The amount of these compounds can be selected such that all the reactive ends of the polymer chains react with compounds of the formula (III), or it is possible to use a deficiency of these compounds. The amounts of the compounds of the formula (Ill) used may cover a wide range. The preferred amounts are within a range from 0.005 to 2% by weight, more preferably within a range from 0.01 to 1% by weight, based on the amount of polymer.

The invention further provides for the reaction of polymers having carbanionic chain ends (obtained from the anionic polymerization or the polymerization with coordination catalysts) first with cyclosiloxanes of the formula (IV) and, in a next step, the reaction of the silanoiate-terminated polymers obtained from the first step with compounds of formula (III) to give carboxylate-terminated polymers. The cyclosiloxanes of the formula (IV) can be used in pure form or as a mixture of different cyciosiloxanes. The amount of the cyclosiloxanes can be selected such that all the reactive ends of the polymer chains react with cyclosiloxanes of the formula (IV), or it is possible to use a deficiency of these compounds. The amounts of the cyclosiloxanes of the formula (IV) used may cover a wide range. The preferred amounts are within a range from 0.002 to 4% by weight, more preferably within a range from 0.005 to 2% by weight, based on the amount of polymer. The amount of compounds of the formula (III) in the subsequent step is ideally selected such that any and all carbanionic ends of polymer chains present and all silanolate-terminated ends of polymer chains react with compounds of the formula (Ill). The preferred ratio of silalactone to cyclosiloxane is 20:1 to 1:1, particular preference being given to a ratio of 10:1 to 1:1, very particular preference to a ratio of 3:1 to 1:1.

In addition to compounds of the formula (III) and cyclosiloxanes of the formula (IV), it is also possible to use the coupling reagents typical of anionic diene polymerization for reaction with the reactive ends of polymer chains. Examples of such coupling reagents are silicon tetrachloride, methyltrichiorosilane, dimethyldichlorosilane, tin tetrachloride, dibutyitin dichloride, tetraalkoxysilanes, ethylene glycol diglycidyl ether, 1,2,4-tris(chloromethyl)benzene, Such coupling reagents can be added prior to, together with or after the compounds of the formula (III).

After addition of compounds of the formula (III) and optionally of coupling reagents, before or during the workup of the inventive silane-containing, carboxylate-terminated polymers, preference is given to adding the customary ageing stabilizers, such as sterically hindered phenols, aromatic amines, phosphites, thioethers. In addition, it is possible to add the customary extender oils used for diene rubbers, such as DAE (Distillate Aromatic Extract), TDAE (Treated Distillate Aromatic Extract), MES (Mild Extraction Solvates), RAE (Residual Aromatic Extract), TRAE (Treated Residual Aromatic Extract), naphthenic and heavy naphthenic oils. It is also possible to add fillers, such as carbon black and silica, rubbers and rubber auxiliaries.

The solvent can be removed from the polymerization process by the customary methods, such as distillation, stripping with steam or application of reduced pressure, optionally at elevated temperature.

The invention further provides for the use of the inventive end group-functionalized polymers for production of vulcanizable rubber compositions.

These vulcanizable rubber compositions preferably comprise further rubbers, fillers, rubber chemicals, processing aids and extender oils.

Additional rubbers are, for example, natural rubber and synthetic rubbers. If present, the amount thereof is typically within the range from 0.5 to 95% by weight, preferably within the range from 10 to 80% by weight, based on the total amount of polymer in the mixture. The amount of rubbers additionally added is again guided by the respective end use of the inventive mixtures. Examples of synthetic rubbers of this kind are BR (polybutadiene), acrylic acid-alkyl ester copolymers, IR (polyisoprene), E-SBR (styrene-butadiene copolymers prepared by emulsion polymerization), S-SBR (styrene butadiene copolymers prepared by solution polymerization), IIR (isobutylene-isoprene copolymers), NBR (butadiene-acrylonitrile copolymers), HNBR (partly hydrogenated or fully hydrogenated NBR rubber), EPDM (ethylene-propylene-diene terpolymers) and mixtures of these rubbers. For the production of car tyres, particularly natural rubber, E-SBR and S-SBR having a glass transition temperature above −60° C., polybutadiene rubber which has a high cis content (>90%) and has been prepared with catalysts based on Ni, Co, Ti or Nd, and polybutadiene rubber having a vinyl content of up to 80% and mixtures thereof are of interest.

Useful fillers for the inventive rubber compositions include all known fillers used in the rubber industry. These include both active and inactive fillers.

The following should be mentioned by way of example:

-   -   finely divided silicas, produced, for example, by precipitation         of solutions of silicates or flame hydrolysis of silicon halides         having specific surface areas of 5-1000, preferably 20-400, m²/g         (BET surface area) and having primary particle sizes of 10-400         nm. The silicas may optionally also be present as mixed oxides         with other metal oxides, such as oxides of Al, Mg, Ca, Ba, Zn,         Zr, Ti;     -   synthetic silicates, such as aluminium silicate, alkaline earth         metal silicates such as magnesium silicate or calcium silicate,         having BET surface areas of 20-400 m²/g and primary particle         diameters of 10-400 nm;     -   natural silicates, such as kaolin, montmorillonite and other         naturally occurring silicas;     -   glass fibres and glass fibre products (mats, strands) or glass         microspheres;     -   metal oxides, such as zinc oxide, calcium oxide, magnesium         oxide, aluminium oxide;     -   metal carbonates, such as magnesium carbonate, calcium         carbonate, zinc carbonate;     -   metal hydroxides, for example aluminium hydroxide, magnesium         hydroxide;     -   metal sulphates, such as calcium sulphate, barium sulphate;     -   carbon blacks: The carbon blacks to be used here are carbon         blacks produced by the lamp black, channel black, furnace black,         gas black, thermal black, acetylene black or light arc process         and have BET surface areas of 9-®m²/g, for example SAF, ISAF-LS,         ISAF-HM, ISAF-LM, ISAF-HS, CF, SCF, HAF-LS, HAF, HAF-HS, FF-HS,         SPF, XCF, FEF-LS, FEF, FEF-HS, GPF-HS, GPF, APF, SRF-LS, SRF-LM,         SRF-HS, SRF-HM and MT carbon blacks, or ASTM N110, N219, N220,         N231, N234, N242, N294, N326, N327, N330, N332, N339, N347,         N351, N356, N358, N375, N472, N539, N550, N568, N650, N660,         N754, N762, N765, N774, N787 and N990 carbon blacks;     -   rubber gels, especially those based on BR, E-SBR and/or         polychloroprene having particle sizes of 5 to 1000 nm.

The fillers used are preferably finely divided silicas and/or carbon blacks.

The fillers mentioned can be used alone or in a mixture. In a particularly preferred embodiment, the rubber compositions comprise, as fillers, a mixture of light-coloured fillers, such as finely divided silicas, and carbon blacks, the mixing ratio of light-coloured fillers to carbon blacks being 0.01:1 to 50:1, preferably 0,05:1 to 20:1.

The fillers are used here in amounts in the range from 10 to 500 parts by weight based on 100 parts by weight of rubber. Preference is given to using amounts within a range from 20 to 200 parts by weight.

In a further embodiment of the invention, the rubber compositions also comprise rubber auxiliaries which, for example, improve the processing properties of the rubber compositions, serve to crosslink the rubber compositions, improve the physical properties of the vulcanizates produced from the inventive rubber compositions for the specific end use thereof, improve the interaction between rubber and filler, or serve for attachment of the rubber to the filler.

Rubber auxiliaries are, for example, crosslinker agents, for example sulphur or sulphur-supplying compounds, and also reaction accelerators, ageing stabilizers, heat stabilizers, light stabilizers, antiozonants, processing aids, plasticizers, tackifiers, blowing agents, dyes, pigments, waxes, extenders, organic acids, silanes, retardants, metal oxides, extender oils, for example DAE (Distillate Aromatic Extract), TDAE (Treated Distillate Aromatic Extract), MES (Mild Extraction Solvates), RAE (Residual Aromatic Extract), TRAE (Treated Residual Aromatic Extract), naphthenic and heavy naphthenic oils and activators.

The total amount of rubber auxiliaries is within the range from 1 to 300 parts by weight, based on 100 parts by weight of overall rubber. Preference is given to using amounts within a range from 5 to 150 parts by weight of rubber auxiliaries.

The vulcanizable rubber compositions can be produced in a one-stage or in a multistage process, preference being given to 2 to 3 mixing stages. For example, sulphur and accelerator can be added in a separate mixing stage, for example on a roller, preferred temperatures being in the range from 30° C. to 90° C. Preference is given to adding sulphur and accelerator in the last mixing stage,

Examples of equipment suitable for the production of the vulcanizable rubber compositions include rollers, kneaders, internal mixers or mixing extruders.

Thus, the invention further provides vulcanizable rubber compositions comprising end group-functionalized polymers having end groups of the formula (I) or (II),

The invention further provides for the use of the inventive vulcanizable rubber compositions for production of rubber vulcanizates, especially for the production of tyres, especially tyre treads, having particularly low rolling resistance coupled with high wet skid resistance and abrasion resistance.

The inventive vulcanizable rubber compositions are also suitable for production of mouldings, for example for the production of cable sheaths, hoses, drive belts, conveyor belts, roll covers, shoe soles, gasket rings and damping elements.

The examples which follow serve to illustrate the invention but have no limiting effect.

EXAMPLES Example 1 Synthesis of styrene-butadiene copolymer, unfunctioalized (Comparative Example)

An inertized 20 l reactor was charged with 8.5 kg of hexane, 1185 g of 1,3-butadiene, 315 g of styrene, 8.6 mmol of 2,2-bis(2-tetrahydrofuryl)propane and 11.3 mmol of butyilithium, and the contents were heated to 60° C. Polymerization was effected while stirring at 60° C. for 25 minutes. Subsequently, 11.3 mmol of cetyl alcohol were added to cap the anionic ends of the polymer chains, the rubber solution was discharged and stabilized by addition of 3 g of Irganox® 1520 (2,4-bis(octylithiomethyl)-6-methylphenol), and the solvent was removed by stripping with steam. The rubber crumbs were dried at 65° C. under reduced pressure.

Example 2 Synthesis of silanolate-Terminated styrene-butadiene copolymer by Reaction with cyclosiloxane (Comparative Example)

The procedure was as in Example 1. In place of the cetyl alcohol, however, an amount of hexamethylcyclotrisiloxane equimolar to that of butyllithium was added (as a solution in cyclohexane) and the reactor contents were then heated to 60° C. for a further 20 minutes.

Example 3 Synthesis of siliane-Containing caboxyl-Terminated styrene-butadiene copolymer by Eeaction with cyclosiloxane and then silalactone (Inventive)

The procedure was as in Example 2. 20 minutes after addition of the hexamethylcyclotrisiloxane, an amount of 2,2-dimethyl-l-oxa-4-thia-2-silacyclohexan-6-one equimolar to that of butyilithium and hexamethylcyclotrisiloxane was added (as a solution in toluene) and the mixture was heated to 60° C. for a further 20 minutes.

Example 4 Synthesis of silane-Containing carboxyl-Terminated styrene-butadiene copolymer having a tertiary Amino Group at the Start of the Chain by Reaction with cyclosiloxane and the n silalactone (Inventive)

The procedure was as in Example 3. Prior to addition of the butyllithium, however, an amount of pyrrolidine equimolar to that of butyllithium was added.

Example 5 Synthesis of silane-Containing hydroxyl-Terminated styrene-butadiene copolymer by Reaction with 1-oxa-2-silacycloalkane (Comparative Example)

The procedure was as in Example 2. In place of the hexamethylcyclotrisiloxane, however, an amount of 2,2,4-trimethyl-1-oxa-4-aza-2-silacyclohexane equimolar to that of butyllithium was added (as a solution in hexane).

The polymer properties of the styrene-butadiene copolymers from Examples 1-5 are summarized in Table 1. It is apparent from Table 1 that the inventive silane-containing carboxyl-terminated polymers of Examples 3 and 4, with the same molecular weight and polydispersity level as the polymers of Comparative Examples 1, 2 and 6, have much higher Mooney viscosities and much reduced cold flow values. Low cold flow values are advantageous, since the corresponding rubbers have a lesser tendency to flow and hence improved dimensional stability in the course of storage.

Examples 6 a-e; Rubber Compositions

Tyre tread rubber compositions comprising the styrene-butadiene copolymers of Examples 1-5 were produced, The constituents are listed in Table 2. The rubber compositions (apart from sulphur and accelerator) were produced in a 1.5 l kneader. The sulphur and accelerator constituents were subsequently mixed in on a roller at 40° C.

TABLE 1 Properties of the styrene-butadiene copolymers of Examples 1-5 Styrene Functionalizing Vinyl content^(a)) content^(a)) Tg^(b)) M_(n) ^(c)) ML1 + 4^(d)) Cold flow^(e)) SSBR from Ex. reagent [% by wt.] [% by wt.] [° C.] [kg/mol] M_(w)/M_(n) ^(c)) [ME] [mg/min] 1 — 51.5 20.9 −23 244 1.10 42 21 (comparative) 2 hexamethyl- 50.6 21.3 −24 239 1.10 41 21 (comparative) cyclotrisiloxane 3 1. hexamethyl- 50.7 21.0 −24 246 1.09 79 0 (inventive) cyclotrisiloxane 2. silalactone 4 1. hexamethyl- 49.9 21.9 −24 183 1.22 56 9 (inventive) cyclotrisiloxane 2. silalactone 5 1-oxa-2- 50.9 21.5 −23 220 1.15 37 25 (comparative) silacycloalkane ^(a))determination of vinyl and styrene contents by FTIR ^(b))determination of glass transition temperature by DSC ^(c))determination of molar mass M_(n) and polydispersity M_(w)/M_(n) by GPC (PS calibration) ^(d))determination of Mooney viscosity at 100° C. ^(e))determination of cold flow at 50° C.

TABLE 2 Constituents of the tyre tread rubber compositions (figures in phr: parts by weight per 100 parts by weight of rubber) Comparative Comparative Inventive Inventive Comparative Example Example Example Example Example 6a 6b 6c 6d 6e styrene-butadiene copolymer from Example 1 70 0 0 0 0 styrene-butadiene copolymer from Example 2 0 70 0 0 0 styrene-butadiene copolymer from Example 3 0 0 70 0 0 styrene-butadiene copolymer from Example 4 0 0 0 70 0 styrene-butadiene copolymer from Example 5 0 0 0 0 70 high-cis polybutadiene 30 30 30 30 30 (BUNA ™ CB 24 from Lanxess Deutschland GmbH) silica (Ultrasil ® 7000) 90 90 90 90 90 carbon black (Vulcan ® J/N 375) 7 7 7 7 7 TDAE oil (Vivatec 500) 36.3 36.3 36.3 36.3 36.3 processing aid (Aflux 37) 3 3 3 3 3 stearic acid (Edenor C 18 98-100) 1 1 1 1 1 ageing stabilizer 2 2 2 2 2 (Vulkanox ® 4020/LG from Lanxess Deutschland GmbH) ageing stabilizer 2 2 2 2 2 (Vulkanox ® HS/LG from Lanxess Deutschland GmbH) zinc oxide (Rotsiegel zinc white) 3 3 3 3 3 wax (Antilux 654) 2 2 2 2 2 silane (SI 69 ® from Evonik) 7.2 7.2 7.2 7.2 7.2 diphenylguanidine (Rhenogran DPG-80) 2.75 2.75 2.75 2.75 2.75 sulfenamide (Vulkacit ® NZ/EGC from Lanxess Deutschland GmbH) 1.6 1.6 1.6 1.6 1.6 sulphur (Chancel 90/95 ground sulphur) 1.6 1.6 1.6 1.6 1.6 sulfonamide (Vulkalent ® E/C) 0.2 0.2 0.2 0.2 0.2

Examples 7 a-e Vulcanizate Properties

The tyre tread rubber compositions of Examples 6a-e according to Table 2 were vulcanized at 160CC for 20 minutes. The properties of the corresponding vulcanizates are listed in Table 3 as Examples 7a-e. The vulcanizate properties of the vulcanized sample from Comparative Example 7a comprising the unfunctionalized styrene-butadiene copolymer are given the index 100. Ail values greater than 100 in Table 3 mean a corresponding percentage improvement in the respective test property.

TABLE 3 Vulcanizate properties Comparative Comparative Inventive Inventive Comparative Example Example Example Example Example 7a 7b 7c 7d 7e Styrene-butadiene copolymer in the vulcanizate: styrene-butadiene copolymer from Example 1 X styrene-butadiene copolymer from Example 2 X styrene-butadiene copolymer from Example 3 X styrene-butadiene copolymer from Example 4 X styrene-butadiene copolymer from Example 5 X Vulcanizate properties: tan δ at 0° C. (dynamic damping at 10 Hz) 100 112 125 125 115 tan δ at 60° C. (dynamic damping at 10 Hz) 100 110 143 145 117 tan δ maximum (MTS amplitude sweep at 1 Hz, 60° C.) 100 115 134 139 117 ΔG* (G*@0.5%-G*@15% from MTS amplitude sweep) 100 159 254 255 189 Resilience at 60° C. [%] 100 113 118 121 114 Abrasion (DIN 53516) [mm³] 100 119 135 130 113

The resiiience et 60° C., the dynamic damping tanδ at 60° C., the tanδ maximum in the amplitude sweep and the module difference ΔG* between low and high strain in the amplitude sweep are indicators of rolling resistance in the tyre. As apparent from Table 3, the vuicanizates of Inventive Examples 7c and 7d feature particularly high improvements in these rolling resistance-relevant properties,

The dynamic damping tanδ at 0° C. is an indicator of the wet skid resistance of the tyre. As apparent from Table 3, the vulcanizates of inventive Examples 7c and 7d feature particularly high improvements in this wet skid-relevant property.

The DIN abrasion is an indicator of the abrasion resistance of the tyre tread. As apparent from Table 3, the vulcanizates of Inventive Examples 7c and 7d feature particularly high improvements in this property. 

1. End group-functionalized polymers, comprising a polymer chain terminated by a silane-containing carboxyl group of the formula (I)

where R¹, R² are the same or different and are each an H, alkyl, alkoxy, oycloalkyl, cycloalkoxy, aryl, aryloxy, alkaryl, alkaryloxy, aralkyl, or araikoxy radical, R³, R⁴ are the same or different and are each an H, alkyl, oycloalkyl, aryl, alkaryl or aralkyl radical, and A is a divalent organic radical.
 2. The end group-functionalized polymers according to claim 1, wherein the silane-containing carboxyl group is a carboxylate of the formula (II)

where n is en integer from 1 to 4, and M is a metal or semimetal of valency 1 to
 4. 3. The end group-functionalized polymers according to claim 1 wherein the silane containing carboxyl group is bonded with the polymer chain via one or more divalent structural elements of the formula (V)

where n=3-6, and where R⁵, R⁶ are the same or different and are each an H, alkyl, cycloalkyl, aryl, alkaryl or aralkyl radical.
 4. The end group-functionalized polymers according to claim 1, wherein the polymers are diene polymers.
 5. The end group-functionalized polymers according to claim 1, wherein the polymer is obtained by reaction of reactive ends of the polymer chain with one or more silalactone functionalizing reagents.
 6. The end group-functionalized polymers according to claim 5, wherein the silalactones are compounds of the formula (III).


7. The end group-functionalized polymers according to claim 1, wherein the polymers have mean molar masses (number-average, MO of 10,000 to 2,000,000 g/mol.
 8. The end group-functionaiized polymers according to claim 1, wherein the polymers have glass transition temperatures of −110° C. to +20° C.
 9. (canceled)
 10. A process for preparing the end group-functionalized polymers according to claim 1, the process comprising adding one or more silalactones to polymers having reactive ends on the polymer chain.
 11. The process according to claim 10, further comprising adding the silalactones to the-polymers after completion of polymerization.
 12. The process according to claim 10, further comprising using an excess or a stoichiometric amount or a deficiency of silalactones, based on the amount of polymer.
 13. The process according to claim 12, wherein the amount of silaiactones is from 0.005 to 2% by weight, based on the amount of polymer.
 14. The process according to claim 10, wherein prior to addition of the silalactones, the process further comprises: polmerizing monomers to form polymer chains having reactive chain ends, and reacting reactive chain ends with cyclosiloxanes of the formula (V)

where n=3-6, and where R⁵, R⁶ in formula (IV) are the same or different and are each an H, alkyl, cycloalkyl, aryl, alkaryl or aralkyl radical.
 15. The process according to claim 14, further comprising reacting the reactive chain ends with 0.002 to 4% by weight of the cyclosiloxanes of the formula (IV) based on the amount of polymer.
 16. The process according to claim 14, wherein ratio of silalactone to cycloslioxane is from 20:1 to 1:1.
 17. (canceled)
 18. Vulcanizable rubber compositions comprising; a) end group-functionalized polymers according to claim 1 and b) ageing stabilizers, oils, fillers, rubbers and/or further rubber auxiliaries.
 19. (canceled)
 20. Moulding produced from vulcanizable rubber compositions comprising the end group-functionalized polymers according to claim
 1. 21. The end group-functionalized polymers according to claim 2, wherein: the silane containing carboxyl groups are bonded to the polymer chair) ends via one or more divalent structural elements of the formula (V)

where: n=3-6, and R⁵, R⁶ are the same or different and are each an H, alkyl, cycloalkyl, aryl, alkaryl or aralkyl radical; and the silane containing carboxyl groups are derived from one or more silalactones by reacting reactive ends of the polymer chain with the silalactones.
 22. The end group-functionalized polymers according to claim 2, wherein: any alkyl, alkoxy, cycloalkyl, cycloalkoky, aryl, aryloxy, alkaryl, alkaryloxy, aralkyl, aralkoxy, or divalent organic radical may contain one or more heteroatoms; the silaiactones are compounds of the formula (III)

and the one or more divalent structural elements of the formula (V) are derived from cyclosiloxanes of the formula (IV))


23. The end group-functionalized polymers according to claim 22, wherein: M is selected from the group consisting Li, Na, K, Mg, Ca, Zn, Fe, Co, Ni, Al, Nd, Ti, Sn, Si, Zr, V, Mo and W; the heteroatoms are O, N, S and Si; the cyclosiloxanes are a member of the group consisting of hexamethylcyclotrisiloxane, actamethylcyclotetrasiloxane, decamethyloyclopentaslioxane or dodecamethylcyclohexasiloxane; the polymers comprise at least one of polybutadiene, polyisoprene, butadiene-isoprene copolymer, butadiene-styrene copolymer, isoprene-styrene copolymer, and butadiene-isoprene-styrene terpolymer; and the polymers have mean molar masses (number-average, M_(n)) of 100,000 to 1,000,000 glenol, and glass transition temperatures of −110° C. to 0° C. 